Well trap structures and bulk-nano environment luminescence centers in CaZnGe2O6:Tb3+ long afterglow phosphor

Authors:B.K. Woo, Y. Li, S.P. Singh
Affilation:Multimedia University, MY
Pages:179 - 182
Keywords:persistent luminescence, long afterglow phosphor, ZnO nanoparticles
Abstract:A long afterglow phosphor CaZnGe2O6:Tb3+ has been prepared by using organic coated luminescence ZnO nanopowder through a high temperature solid-state reaction route. This new CaZnGe2O6:Tb3+ long afterglow phosphor sample emits the Tb3+ green fluorescence 543 nm emission corresponding to 5 D 4 ⟶ 7 F 5 transition under UVA 350 nm illumination. The organic coated luminescence ZnO nanopowder serves to construct shallow well trap for the Tb3+ dopant and to minimize electron leakage of well traps. By adjusting the mass ratio of both the bulk ZnO powder (<1000 nm size) and the organic coated luminescence ZnO nanopowder (5-10 nm size), depth of well traps that dictate luminescence and afterglow properties could be controlled. The optimized long afterglow phosphor sample was found to be made of 70% gm-weight of bulk ZnO powder and 50% gm-weight of organic coated luminescence ZnO nanopowder or CaZn0.83Ge2O6:Tb3+ phase compound that exhibit afterglow longevity of longer than 3 hours. Therefore, phosphorescence effect is best explained based upon well trap structures model and structure lattice defects play an important role in influencing persistent luminescence phenomena.
ISBN:978-1-4822-0581-7
Pages:830
Hardcopy:$209.95
 
Order:Mail/Fax Form
Up
© 2014 Nano Science and Technology Institute. All Rights Reserved.
Terms of Use | Privacy Policy | Contact Us | Site Map