Annealing effects on electrical and optical properties of

Authors:S.M. Faraz
Affilation:NED University of Engineering & Technology, PK
Pages:68 - 71
Keywords:nanoelectronics, nanodevices, ZnO nanorods
Abstract:Annealing effects on the electrical and optical properties of ZnO nanorods/Si heterojunction diodes are studied. ZnO nanorods are grown on p-Si substrate by aquous chemical growth (ACG) method .As grown samples were annealed at 400 and 600 oC in air, oxygen and nitrogen ambient. Structural, optical and electrical characteristics are studied by Scanning Electron Microscopy (SEM), Photoluminescence (PL), Current–Voltage (I-V) and Capacitance-Voltage (C-V) measurements.Well aligned hexagonal–shaped vertical nanorods of a mean diameter of 160-200nm and approximately 1.2μm high are revealed in SEM. PL spectra indicated higher ultraviolet (UV) to visible emission ratio with a strong peak of near band edge emission (NBE) centered from 375-380 nm and very weak broad deep-level emissions (DLE) centered from 510-580 nm. It is observed that the UV emission is strongly enhanced after annealing in air, nitrogen and oxygen at 400 oC. To our knowledge this is the first report on simultaneous study of annealing effects on the optical and electrical properties of ZnO nanorods at 400 and 600 oC in air, oxygen and Nitrogen.
Annealing effects on electrical and optical properties ofView PDF of paper
Order:Mail/Fax Form
© 2017 Nano Science and Technology Institute. All Rights Reserved.
Terms of Use | Privacy Policy | Contact Us | Site Map